Products

PRIMERS

SEALER BV

Solvent-free, pure resin-based primer, to protect against moisture by creating vapor barrier on any dry or wet surface. It also performs under water. It can be diluted with BV solvent.

Features:

  • Presentation: Metallic can (A + B) 4 Liters
  • Mixture: 100 Comp A – 60% Comp B.
  • Color Blend: Gray
  • Solids by weight: 100%
  • Output: 0.4 – 1 kg / m2 according to porosity
  • Mixture Life: 1 Hour to 20º
  • Adhesion time: 3 Hr at 20º
  • Adherence to Concrete:> 25kg / cm2
  • Storage: 5º to 40º max 12 months.

PRIMER CEMENT

Concentrated water sealant without acrylic emulsion TAC without organic solvent, to be applied in porous areas or in need of hardening. Product to use, it admits dilution with water 1 / 1.1 / 2.1 / 3 according to porosity.

Features:

  • Presentation: 5 liter plastic bottle
  • Color Blend: Milky
  • Output: +/- 20m2 / Liter according to absorption
  • Adherence: Very good according to support, max. Effectiveness at 12 Hours.
  • Outdoor Resistance: Aliphatic, UV resistant
  • Specific weight: 1g / cc
  • Frost Stability: Good
  • Storage: between 5º and 40º max 12 months.
  • Not toxic, flammable or dangerous

 

IN ACCORDANCE WITH UNE-EN 1262

PRIMER CEMENT TACK

Bonding sealer with a permanent TACK, acrylic emulsion without organic solvent, able to create anchorage / adhesion in any type of support. Product to use, admits dilution with  water 1 / 1.1 / 2.1 / 3 according to porosity.

Features:

  • Presentation: 5 liter plastic bottle
  • Mixture Color: Milky
  • Output: +/- 20m2 / Liter according to absorption
  • Adherence: Very good according to support, max. Effectiveness at 12 Hours.
  • Outdoor Resistance: Aliphatic, UV resistant
  • Specific weight: 1g / cc
  • Frost Stability: Good
  • Storage: between 5º and 40º max 12 months.
  • Not toxic, flammable or dangerous.

 

IN ACCORDANCE WITH UNE-EN 1262

SUPPORT CORRECTORS

ELASTIC

Flexible and waterproof bicomponent mortar (20 kg + 10 Liters) to correct supports with retraction fissures with two layers and intermediate mesh in both mortar concrete, wood, parquet, pallet, plaster, self-leveling mortar … Resistance to positive pressure. Waterproofing of concrete tanks for water, including drinking water. Waterproofing of showers, baths, swimming pools … Waterproof coating of concrete surfaces exposed to the action of water and to the chemical aggression of external agents, such as salts, de-icing, chlorides … Apply 2 hands with 80 gr intermediate mesh.

Features:

  • Presentation: Paper bags of 20Kg + 10 Liters.
  • Color: White and Gray
  • Dosage: A + B (2/1)
  • Resting time after kneading: 5 min.
  • Mixture Life: 60 minutes
  • Application thickness: 2 mm per layer
  • Start of setting: 4 hours
  • Resting time between layers: 4-5 hours
  • Waiting time for tank filling: ≥28 days
  • Coating – painting:> 6 days
  • Apply at temperatures between 10º and 30º
  • Do not apply with risk of rain or strong wind
  • Traction adhesion: ≥1.5 MPa
  • Dilution index: ≤3
  • Dilution odor: ≤5
  • Conductivity: (μS / cm) 325
  • PH (μPH): 8.4
  • Properties in traction:
  • Strength: 1.6 MPa
  • Elongation: 65%

* Certificate of Potability
* UNE-EN-1504-2

PLASTIC

Deformable mortar, with compressive strength, for repair and / or slight correction of planimetry or bonding of support changes. Application to two layers accompanied by a fiber mesh of 80 Gr intermediate between layers.

Features:

  • Presentation: 25 kg paper bags, 48 bags pallets
  • Mixing: Until a homogeneous kneading (between 25 and 30%)
  • Initial adhesion: ≥ 1.0 N / mm2
  • Adhesion after immersion in water: ≥ 1.0 N / mm2
  • Adhesion after heat aging: ≥ 1.0 N / mm2
  • Adhesion after freeze-thaw cycles: ≥ 1.0 N / mm2
  • Adhesion open time: ≥ 0.5 N / mm2
  • Deformation: ≥ 5 mm
  • Sliding: ≤ 0.5 mm

 

 

* Tests according to UNE- EN 12004

PLASTIC PRESS

Waterproofing mortar for negative pressure waterproofing repairs and waterproofs severe cracks, suitable on supports with small movements. Suitable for receiving paint or cementitious coating. Resistant to contact with aggressive waters. Spectacular resistance to negative pressure, essential for swimming pools.

Features:

  • Presentation: 25 kg anti-humidity paper bags, + 10 liters. Pallets of 48 bags
  • Bulk density: 1.3 g / cm3
  • Density in paste: 1.6 g / cm3
  • Compression:> 30 N / mm2
  • Flexion:> 6 N / mm2
  • Determination of transverse deformation: 2.5 mm
  • Waterproofing DIN 1048: Waterproof
  • Adhesion on concrete: 1.6 MPa
  • Cementitious junction bridge
  • Negative pressure resistance: 15 bar
SUPPORT REPARATORS

GENERAL APPLICATION RECOMMENDATIONS FOR SUPPORT REPARATORS

  • In areas where the iron frame appears, clean with sandblast or using a metallic brush, cover with MORTAR ANTICORROSIÓN and allow to dry at least 1 hour.
  • Do not apply on smooth concrete supports (before roughing and opening pores).
  • Do not use by casting for fillings.
  • Remove the deteriorated concrete, with possible detachment until reaching a solid support.
  • Placement of fiberglass or metallic mesh in areas at risk of cracking.
  • The supports must be flat, healthy, stable and resistant, free of dust, plaster, paint …
  • In hot weather and with a dry wind, the surface must be humidified before and 24 hours after the application of the coating, to favor the curing of the mortar and to avoid cracks and cracks, as well as the formation of dusty areas. At higher temperatures, these phenomena intensify.
  • On walls without absorption, walls, concrete … use PRIMER CEMENT or bonding PRIMER CEMENT TACK.
  • Avoid the application of the coating with low temperatures, high humidity, rain … In the hours that follow after the application of the mortar increases the risk of appearance of efflorescence by carbonation.

ANTICORROSION REPAIR

Repair mortar, armor passivator in cementitious base. Excellent protection of steel bars. Easy to apply, no retraction.

Features:

  • Presentation in bags of 5 Kg (color of the mixture: black)
  • Ouput: 0.200 kg of mortar / m2 (14 mm steel bar)
  • Application temperatures: 10 – 30ºC
  • Apparent density powder: 1.3 g / cm3
  • Kneading water: ± 25%
  • Density of mass: 1.5 g / cm3
  • Pot Life: 30 minutes
  • Time between layers: 3-4 hours (20ºC)
  • Full setting: 24 hours (20ºC)
  • Storage 6 months from the date of manufacture.

 

* CAN NOT BE LEFT TO EYE SIGHT. COVER WITH ANY OTHER REPAIRING MORTAR.

R2 REPARATOR

Filling of cracks and external cladding of buildings, regularization of walls, defective surfaces, such as concrete joints, formwork, gravel nests, repair of cisterns , Canals, ditches … Without retraction, thixotropic. High immediate resistance, fibrated. For high thicknesses.

Features:

  • Presentation in paper bags of anti-humidity of 25 Kg. • Pallets of 48 bags
  • Color: white and gray.
  • Ouput: 1.4 kg / m2 and mm thick
  • Apparent density powder: 1.4 g / cm3
  •  Kneading water ratio: 20%
  • Mass density: 1.7g / cm3
  • Compressive strength: ≥ 15 MPa
  • Flexotraction: ≥ 5N / mm2
  • Adherence by direct traction: ≥ 1MPa
  • Ice-melt in salts: ≥ 0.8 Mpa
  • Capillary absorption ≤ 0.5 kg / (m2x h05)
  • Resting time after kneading: 5 min.
  • Approximate kneading life: 1 hour (20ºC)
  • Maximum thickness per layer: 30-35 mm
  • Waiting time between layers: 3-4 hours

 

ACCORDING TO STANDARD EN 1504-3

R3-R REPARATOR

Mortar for repairing columns, beams, overhangs, pillars, balconies, degraded areas of concrete …, for the corrosion of the reinforcement and that a fast setting is required. Filling of cracks and external cladding of buildings. For repairs that require an urgent commissioning, such as revocation edges, embedding of registration boxes or pipes and repairs of coke. Indoors and outdoors. Without retraction, thixotropic. High immediate resistance, bundle.

Features:

  • Presentation: paper bags of 25 kg anti-humidity. • Pallets of 48 bags
  • Color: White and Gray
  • Yield: 1.4 kg / m2 and mm thick
  • Apparent density powder: 1.4 g / cm3
  • Mixing water: 22% (Between 5 and 5.5 liters of running water)
  • Density by mass: 1.7 g / cm3
  • Traction adhesion: ≥ 1.5 MPa
  • Compression 28 days: ≥ 25 MPa
  • Flexotraction: ≥ 7.0 MPa
  • Modulus of elasticity in compression: ≥ 15 GPa
  • Ice-melt in salts: ≥ 1.5 MPa
  • Capillary absorption: ≤ 0.5 kg / (m2xh05)
  • Resting time after kneading: 5 min.
  • Dough life: 30-60 min. (20 ° C)
  • Maximum thickness tolerated: 3 -15 cm (in layers of 5cm)
  • Setting start: 2-4 hours

 

ACCORDING TO STANDARD EN 1504-3

R4 REPARATOR

Repair mortar for columns, jigs, overhangs, pillars, balconies, degraded areas of concrete …, for the corrosion of reinforcement and fast setting is required. Reconstruction of the coating layer of the reinforcement in reinforced concrete structures. Repair of surfaces exposed to strong abrasion (canals, pavements, ramps …) Regularization of walls, tunnels … Restoration and repair of viaducts on roads. Indoors and outdoors. Without retraction, thixotropic. High immediate resistance, bundle.

Features:

  • Presentation: in paper bags of 25 kg anti-humidity. • Pallets with 48 bags.
  • Color: White and gray.
  • Yield: 1.4 kg / m2 and mm thick
  • Apparent density powder: 1.4 g / cm3
  • Density by mass: 1.7 g / cm3
  • Kneading water: 18%
  • Traction adhesion: ≥ 2 MPa
  • Compression 28 days: ≥ 45 MPa
  • Flexotraction: ≥ 10 MPa
  • Traction breakage: ≥ 2 MPa
  • Modulus of elasticity in compression: ≥ 20 GPa
  • Ice-melt in salts: ≥ 2.0 MPa
  • Capillary absorption: ≤ 0.5 kg / (m2xh05)
  • Determination of chlorides: 0.00%
  • Resting time after kneading: 5 min.
  • Dough life: 60 min. (20 ° C)
  • Maximum thickness tolerated: 3 -15 cm (in layers of 5cm)
  • Setting start: 2-4 hours

ACCORDING TO STANDARD EN 1504-3

FLUID REPARATOR

Fluid and expansive filling mortar, by pouring under support and distribution plates. Filling of rigid joints between elements of conventional and prefabricated concrete. Anchors of metallic elements (reinforcements, bolts, machinery …), metal poles and concrete. Support of bridges and cranes, by means of casting under plates. Also suitable for injection and pumping.

Features:

  • Presentation: in paper bags of 25 kg anti-humidity. • Pallets with 48 bags.
  • Gray.
  • Yield: 1.4 kg / m2 and mm thick
  • Apparent density powder: 1.4 g / cm3
  • Density by mass: 1.7 g / cm3
  • Kneading water: 18%
  • Traction adhesion: ≥ 2 MPa
  • Flexotraction: ≥ 10 MPa
  • Compression 28 days: ≥ 45 MPa
  • Traction breakage: ≥ 2 MPa
  • Dynamic modulus of elasticity: ≥ 20 GPa
  • Ice-thaw: ≥ 2.0 MPa
  • Capillary absorption: ≤ 0.5 kg / (m2xh05)
  • Dough life: 45 – 60 min. (20 ° C)
  • Application thickness: 40 – 60 mm
  • Open time:> 30 min.
  • Setting start: 90 – 150 min.
  • Flexotraction: ≥ 7.8 N / mm2
  • Compression 28 days: ≥ 30 N / mm2
  • Dynamic modulus of elasticity: ≥ 15 GPa

Added application recommendations:

  • Application temperature between 5 -35ºC
  • For fillings higher than indicated, add maximum gravel (6-12mm.) In a proportion of 2 to 1 gravel.
  • At low temperatures, water should be used at more than 18 ° C.
  • In hot weather, do not expose the material to the sun and use cold water for mixing.

ACCORDING TO STANDARD EN 1504-3

INSTAND REPARATOR

Quick setting mortar to stop waterways. Cracks, basements, deposits. Even with high pressures.

Features:

  • Presentation: 5 liter drum.
  • Gray
  • Density in powder: 1.3 g / cm3
  • Kneading water: 20-30%
  • Bulk density: 1.8 g / cm3
  • Behavior to fire: 1.8 g / cm3
  • M.P .: 12
  • Kneading time: less than 1 minute
  • Start of setting: from 0.5 to 1 min.
  • Setting time: from 1 to 3 min.
  • Waiting to coat: 24-48 hours
  • Thickness of application: from 2 to 10 cm.
  • Not suitable for filling large areas.
  • Wear rubber gloves
  • Does not resist the cracking of the support
  • Setting fast in a few seconds
  • Waterproof and resistant
  • Free of chlorides
  • Hydraulic mortar, without retraction and coating.

 

ACCORDING TO STANDARD EN 1504-3

SELF-LEVELING

For further installation of parquet, ceramic or carpet

Precautions before placing self-leveling compound:

Do not apply in:

  • Cracked supports. Repair before with ELASTIC PRESS
  • Outdoor floors.
  • With room humidity rate> 85%.
  • On wet floors subject to continuous raising damp.
  • In degraded, fragile or unstable floors.
  • Under floor heating in service (stop heating 24 hours before and start up after 48 hours after the completion of work).
  • About lime-based mortars (calcium sulphate).

General conditions of the support in self-leveling application:

  • The support must be solid and hard, dry, free of dust, disintegrable areas, paints, waxes and oils, oxides, gypsum remainders …
  • In all cases, on new or old concrete and compression> 25 N / mm2, mill until Arid appears, aspirate and if necessary reinforce with Silicate Hardener.
  • Avoid application with air stream.
  • Do not apply to fissured concrete, degraded or with possibility of movements …
  • On new concrete, it must be completely set, ≥ 28 days.
  • Respect the expansion of joints, by cutting or profile installation (patches of maximum, 16-20 m2).

General conditions of application of self-leveling agents:

  • Always respect the same ratio of water during kneading.
  • Do not add any additives to the mortar.
  • Respect the minimum thicknesses required according to the types of support.
  • Respect, perimetral joint (min 5 mm), dilation (16-20 m2) and fractionation.
  • Application temperatures 5 ° C to 30 ° C.

LEVEL LIGHT

Low density cementitious self-leveling mortar, normal setting and compensated shrinkage. Suitable for leveling floors in thick layers, where a high thermal insulation is required, as well as a reduced weight of the slab. Reduce the weight of the slab by 50% approx. With respect to a conventional self-leveling mortar. To level and smooth thickness differences between 30 – 150 mm. Light traffic and heating floors. Indoors.

Features:

  • Presentation: Anti-humidity paper bags of  25 Kg.
  • Palets of 48 bags.
  • Color : Gray
  • Output: 14,2 ltrs. / m2 & cm of thickness
  • Temperature of application: 5 – 35 ºC
  • Kneading time: 2 – 3 minutes
  • Resting time before to apply: 2 minutes
  • Kneading life : 20 – 60 minutes
  • Dry to the touch: 4 to 12 hours
  • Sanding time: > 16 hours
  • Coating time: 2 to 5 days
  • Epoxy resin: 15 days
  • Powder density: 825 ± 25 kg/m3
  • Kneading density: 1500 ± 25 kg/m3
  • Hardened product density: 1066 ± 25 kg/m3
  • Kneading water ratio: 30% (aprox. 5,5 lts. agua)
  • Flexibility resistance: ≥ 4.0 N/mm2
  • Compression resistance: ≥ 20 N/mm2
  • Minimum layer thickness: 30 mm
  • Powder density: 500 ± 25 kg/m3
  • Kneading density: 1900 ± 25 kg/m3
  • Hardened product density: 1400± 25 kg/m3
  • Minimum layer thickness: 10 mm

LEVEL BASIC

Fluid self-leveling in gray color for leveling of preparation or filling for later installation of ceramic, wood, pallet, artificial grass, carpet …

Features:

  • Presentation: Anti-humidity paper bags of 25 Kg.
  • Palets of 48 bags.
  • Color: White
  • Ouput: 11 kg/m2 y cm
  • Kneading water ratio (in lab): 21 %
  • Flexibility resistance (at 28 days): > 10,0 N/mm2
  • Compression resistance (at 28 days): > 40,0 N/mm2
  • Böhme wastage UNE-EN 13892-3: 17,9 cm3/50cm2
  • Wastage UNE-EN 13748-1: < 20,0 mm
  • Concrete adherence: > 1 N/mm2
  • Impact resistance, UNE-EN 12633
  • Drop height: >1500 m
  • IR rate: IR=14,7 N•m
  • Adherencce on ceramic support: 0,98 N/mm2
  • Fire behaviour: A1 euroclass
  • Output: 15kg/m2 y cm
  • Kneading water rate (in lab): 20 %
  • Flexibility resistance (at 28 days): > 3.5/mm2
  • Compression resistance (at 28 days): > 1.5 N/mm2

LEVEL FLOOR INDOOR

Magnificent porcelanic self-leveling, fluid, for interior, colored in mass according to color chart and as finish. Suitable for pumping.
Can be supplied colored.

Features:

  • Presentation: Anti-humidty paper bags of 25 Kg.
  • Palets of 48 bags.
  • Color: According to color chart or as per requirement.
  • Output: 11 kg/m2 and cm
  • Kneading water ratio (in lab): 20%
  • Kneading time: 2-3 minutes
  • Resting time before to apply: 2 minutes
  • Kneading life : 25-30 minutes
  • Setting start: 45 minutes
  • Dry to the touch: 4-5 hours (20ºC)
  • Walkable (pedestrian): > 8 hours
  • Sealing time with PRIMER VARNISH: 24 hours
  • Sealing time with AQUA VARNISH: > 12 hours and humidity < 4%
  • Tiling, carpet, parquet, o cement bases: < 4% humidity
  • Solvent based varnishing from 7 days with humidity < 4%
  • Flexibility resistance (28 days): > 12,0 N/mm²
  • Compression resistance (28 days): > 45,0N/mm²
  • Böhme wastage: UNE-EN 13892-3:17,9cm3/50cm²
  • Wastage UNE-EN 13748-1: < 20,0 mm
  • Concrete adherence: 1 N/mm²
  • Adherence on ceramic support: 0,98 N/mm²
  • Impact resistance, UNE-EN 12633:
  • Drop height: >1500 mm
  • IR rate: IR=14,7 N•m
  • Fire behaviour: A1 euroclass
  • Designation: EN 13813: CT- C40- F10- A22
  • Color: According color chart.

LEVEL FLOOR OUTDOOR

Self-leveling without retraction, SEMI-FLUID, for outdoor, coloured in mass according chart.

Features:

  • Presentation: Anti-humidity paper bags of 25 kg
  • Output: 1.5 kg/m2 y mm of thickness
  • Color: gray & white.
  • Kneading time: 2-3 minutes
  • Resting time before to apply: 2 minutes
  • Kneading life : 20 minutes
  • Dry to the touch: 2 – 4 hours
  • Coating time: 24 – 36 hours
  • Sanding time: from 24 hours
  • For painting application: ≥15días
  • Consistency: fine powder
  • Powder density: 1.5 g/cm3
  • Mass density: 2 g/cm3
  • Flexion: ≥ 5 N/mm2
  • Compression: ≥ 20 N/mm2
  • Hardness: 100 N/mm2
  • Bhöme wastage: 21.0 cm3/50 cm2
  • Output: 1.8 kg/m2 y mm de espesor
MICRONIZED

BASE PORCELANIC

Cementitous base with micronized quartz, excellent workability and hardness by combination of resins of last generation developed in exclusivity for the products manufactured by SATINE. Base coat prior installation of any micronized material. No sanding required thanks to his spectacular calibration.

Features:

  • Output: 500 to 700 Gr per layer and m2. (According support)
  • Compression resistance: 55 N/mm2 (550 kg/cm2)
  • Presentation: Plastic buckets of 20 Kg Monocomponent (for mixture with water)
  • Plastic buckets of 20 Kg Bicomponent (for mixture with resina micro)
  • Palets of 115 * 115 with 36 cubos.
  • Liquid mixture: Until achieve an homogeneous mixture (20 to 25%)
  • Resting time before to apply: 2 minutes and reknead.
  • Mixture life: 7 Hours.
  • Open time: 2 Hours
  • Maximum thickness per layer: 0.5 a 1 mm.
  • Fresh to fresh application allowed.

 

 ACCORDING NORMATIVE UNE-EN-13813:2003

 

*According the water ratio, with less liquid (compact kneading) we will achieve a more homogeneous finish, without shades, rustic and very resistant, suitable as fair-faced finish, or as preparation for application of porcelanic microcement topcoat.

*According temperature / humidity / working system or habits, can adapt the product in terms of drying, hardness, workability and granulometry as per customer requirements.

FINO PORCELANIC

Cement based micronized quartz of impalpable granulometry with high resistance, without cracks, free of dust at the sanding and with extreme adherence. Excelent workability and hardness by combination of resins of last generation developed in exclusivity for the products manufactured by SATINE. (This product can be manufactured with or without shade effects chemically controlled)

Features:

  • Output: 200 to 300 Gr per layer and m2.(according support)
  • Compression resistance: 45 N/mm2 (450 kg/cm2)
  • Presentation: 20 Kg Monocomponent (for mixture with water)
  • 15 Kg Bicomponent (for mixture with resina micro)
  • Palets of 115 * 115 with 36 cubos.
  • Liquid mixture: Until to achieve an homogeneous kneading.  ( 30 to 35%)
  • Resting time before to apply: 2 minutes and reknead.
  • Mixture life: 7 Hours.
  • Open time: 2 Hours
  • Maximum thickness per layer: 0.1 a 0.5 mm.

 

ACCORDING NORMATIVE UNE-EN-13813:2003

 

*For homogeneous kneading like painting mode.

 

*For finishing with Solvent / Aqua Varnish prior Primer Varnish.

 

*According temperature / humidity / working system or habits, can adapt the product in terms of drying, harndess, workability and granulometry as per customer requirements.

 

*Color according chart. Can be coloured in mass or separately.

MEDIUM PORCELANIC

Cementitious base quartz of controlled granulometry and high strength for a one-coat finish without French-style stuccoed water. Extreme adhesion. Excellent workability and hardness by combining state-of-the-art resins developed exclusively for products manufactured by SATINE.

Features:

  • Yield: 300 to 500 gr per layer and m2 (depending on the support)
  • Compressive strength: 50 N / mm2 (500 kg / cm2)
  • Presentation: 20 Kg Monocomponent (for mixing with running water)
  • 20 Kg Bicomponent (for mixing with micro resin)
  • Pallets 115 * 115 with 36 cubes.
  • Liquid mixture: To obtain a homogeneous paste. (30 to 35%)
  • Resting time before applying: 2 minutes and re-kneading.
  • Mix Life: 7 Hours.
  • Open Time: 2 Hours
  • Maximum thickness per layer 0.2 to 0.5 mm.

 

ACCORDING TO THE STANDARD UNE-EN-13813: 2003

* According to the water mixture, with less liquid (compact kneading) we will achieve a smoother finish and an extra fine finish after lacquering, without water and very resistant, or more liquefied, achieving a somewhat striated and rustic effect while resistant .

* For finishing with solvent / water lacquer prior Primer bernis.

* According to temperature / humidity / work system or customs, the product can be adapted in terms of drying, hardness, workability and granulometry to the customer’s taste.

PORCELAIN RUSTIC (MICRO CONCRETE / MICRO CONCRETE)

High resistance micronized quartz for commercial, industrial or garden finishes. Extreme adhesion. Excellent workability and hardness by combining state-of-the-art resins developed exclusively for products manufactured by SATINE.

Features:

  • Yield: 300 to 600 gr per layer and m2 (depending on the support)
  • Compressive strength: 55 N / mm2 (550 kg / cm2)
  • Presentation: 20 Kg Monocomponent (for mixing with running water)
  • 20 Kg Bicomponent (for mixing with micro resin)
  • 115v * 115 pallets with 36 cubes.
  • Liquid mixture: To obtain a homogeneous paste. (25 to 30%)
  • Resting time before applying: 2 minutes and re-kneading.
  • Mix Life: 7 Hours.
  • Open Time: 2 Hours
  • Maximum thickness per layer 0.5 to 1 mm.

 

ACCORDING TO THE STANDARD UNE-EN-13813: 2003

* According to the water mixture, with less liquid (compact kneading) we will achieve a smoother finish and an extra fine finish after lacquering, without water and very resistant, or more liquefied, obtaining a striated effect and rustic while resistant and non-slip .

* For finishing with solvent / water lacquer prior Primer bernis.

* According to temperature / humidity / work system or customs, the product can be adapted in terms of drying, hardness, workability and granulometry to the customer’s taste.

MICRO RESIN

Acrylic emulsion free of ammonia, elastic and hardening for special mixing as component B of micronized bicomponent products.

Features:

  • Presentation: 5 Liters
  • Solids content: 35%
  • PH: 9.0 -10.0
  • Milky appearance
  • Viscosity: 300
  • Conservation: fresh places between 2º and 35º max 12 months.

 

CONFORMING STANDARD UNE-EN 1262

* Any of these products can be monocomponentes or bicomponetes, of being of the latter, to mix with Micro Resin until obtaining a homogenous kneading.

* For finishing in facades with hydrorepente, in swimming pools with varnish pool or cream pool, without primer, rest of finishes polyurethane water or previous solvent primer.

TADELAKT

Moroccan marmoreal micro-mortar. Composed of hydraulic lime, marmolina and limestone.

Features:

  • Yield: 3 kg per layer and m2 (depending on support)
  • Compressive strength: 3 N / mm2 (30 kg / cm2)
  • Presentation: 20 Kg Monocomponent (for mixing with running water)
  • Pallets 115 * 115 with 36 cubes.
  • Breathable 100%
  • Liquid mixture: To obtain a homogeneous paste. (25 to 30%)
  • Resting time before applying: 2 minutes and re-kneading.
  • Mix Life: 24 Hours.
  • Open Time: 6 Hours
  • Maximum thickness per layer 2 mm.

* For subsequent application of black finishing soap

* According to temperature / humidity / work system or customs, the product can be adapted in terms of drying, hardness, workability and granulometry according to the client’s taste

* Colors per letter

METALLIC

Self-extinguishing single-component ferritic powder

Single-component copper powder

Single-component aluminum powder

Monocomponent bronze powder

GLAZINGS

Glazings gold ready to use

Glazings gold ready to use

Glazings silver ready to use

Glazings silver ready to use

SEAMLESS TERRAZO

STONE FRESH

Fluid concrete based on marble, granite … for the formation of continuous floors on fresh concrete. Moderate light and heavy traffic. Indoors and outdoors. On fresh concrete (fresh on fresh) For thicknesses of 10 to 15 mm on fresh concrete and a minimum thickness of the system (concrete + finishing): 6 cm in all points. Polished or bush finish.

Features:

  • Presentation: Paper bags of 25 kg, anti-humidity.
  • 1200 kg pallets (48 bags)
  • Yield: 12-14 kg / m2 and cm of thickness Kneading with concrete mixer.
  • Dough life: 30-45 minutes.
  • Setting start: same as a concrete.
  • Dry to the touch:> 3 hours.
  • Transitable (pedestrian):> 10 hours.
  • Time for dry polishing:> 7 days – Kneading water (in the laboratory): 14%
  • Resistance to bending:> 9 N / mm2
  • Compressive strength:> 55 N / mm2
  • Wear UNE-EN 13892-4: 18 cm3 / 50 cm2
  • Sliding resistance according to CTE: Class 1
  • Adhesion on concrete:> 1,5 N / mm2
  • Adhesion on non-absorbent support with joining bridge:> 0.9 N / mm2
  • Impact resistance, UNE-EN 12633
  • Drop height:> 1500 m
  • IR value: IR = 14.7 N · m
  • Behavior in fire: A1 euroclass

 

Designation: EN 13813: 2003 – CT-C40-F7-A22

PRECAUTIONS / DO NOT APPLY
With ambient humidity> 85%, with direct sunlight and extreme temperatures.
In different thicknesses.
On fresh strength concrete On wet floors subject to continuous lifts of humidity (for the version of applied on dry)
About calcium sulfate mortars or lime base.

STONE

Fluid concrete based on crystals and quartz. Moderate light and heavy traffic. For interiors and on supports of mortars and concretes of high resistance to compression (> 35 N / mm2). On substrates of cementitious base … to apply in thicknesses of 12 to 15 mm (punctual zones maximum thickness of 20 mm). For polished finish. On completely dry supports.

Features:

  • Presentation: Paper bags of 25 kg, anti-humidity.
  • 1200 kg pallets (48 bags)
  • Yield: 11-12 kg / m2 and cm thickness
  • Kneading and pumping transport
  • Dough life: 20 minutes
  • Dry to the touch: 5 to 7 hours
  • Transitable (pedestrian):> 8 hours
  • Dry polishing time:> 7 days
  • Kneading water (in laboratory): 17%
  • Resistance to bending:> 9 N / mm2
  • Compressive strength:> 55 N / mm2
  • Wear UNE-EN 13892-4: 18 cm3 / 50 cm2
  • Sliding resistance according to CTE: Class 1
  • Adhesion on concrete:> 2 N / mm2
  • Adhesion on non-absorbent support with joining bridge:> 0.9 N / mm2
  • Impact resistance, UNE-EN 12633;
  • ** Drop height:> 1500 m
  • ** IR value: IR = 14.7 N · m
  • Behavior in fire: A1 euroclass

Designation: EN 13813: 2003 – CT-C40-F7-A22

PRECAUTIONS, DO NOT APPLY:
Outdoor floors
Wet floors subject to continuous lifts of humidity. Do not apply fresh on fresh, let set for 28 days.
Fragile or unstable soils.
Under floor heating in service (stop the heating 24 hours before and start up after 48 hours after the completion of work.
On mortar based on calcium sulphate (anhydrite) or lime base.

LACQUER AND VARNISHES

PRIMER VARNISH

Water-based resin specially developed for the sealing of indoor and outdoor pavements, with aliphatic acrylic emulsion, which is mainly used for the decorated finishing of passable pavements.

Features:

  • Presentation: 5 Liters
  • Specific weight 1.02 g / cc.
  • Dry to the touch 1 hour.
  • Stability to frost Good.
  • Stability to the outside Aliphatic.
  • Stability to traffic High.
  • Aliphatic.
  • Resistance to saponification Very good
  • Adhesion Clean and dry porous surfaces.
  • Finish Silky.
  • Minimum Layer Thickness Impregnant
  • Yield 12 ± 15 m² / kg. According to support.

* Recommended to use trowel or sponge trowel

AQUA VARNISH

Varnish to the water of high resistance and high traffic for floors. Matte, gloss or satin. Specially developed for the sealing of floors in interior and exterior, with emulsion of acrylic polyurethane, aliphatic. It is mainly used for the decorated finishing of passable pavements.

Recommended in the finishing of new pavements or rehabilitation of pavements of fused concrete, self-leveling, microcements, printed concrete

Features:

  • Homogenate mechanically
  • Presentation: A + B 5 Liters
  • Mixture: component B at 3/1 on component A
  • Specific weight 1.02 g / cc.
  • Dry to the touch 1 hour.
  • Stability to frost Good.
  • Stability to the outside Aliphatic.
  • Stability to traffic High. Aliphatic.
  • Resistance to saponification Very good
  • Adhesion Clean and dry porous surfaces.
  • Matte finish.
  • Minimum Layer Thickness Impregnant
  • Yield 8 ± 12 m² / kg. According to support.

VARNISH SOLVENT

Finishing varnish, polyurethane and non-yellowing acrylic (Component A + B 4 Liters) based on aliphatic isocyanate and polyacrylate resins that harden by chemical reaction at room temperature.

Features:

  • Presentation: A + B 4 Liters
  • Mixture: component B at 3/1 on component A
  • Transparent color
  • Finish: Matte / Satin / Colored on request
  • Density: ≤ 1.4
  • Solids: 68%
  • Resistance: 9K
  • Pot Life: 3 h.
  • Product Viscosity: 20 “± 5” FORD Cup 8
  • Mixing Viscosity: 42 “± 5” FORD Cup 4
  • Temp. Application: + 5º to 40º
  • Drying: 3 Hours
  • Application between layers: 12 hours
  • Dry Film Thickness: 100 ± 20 microns
  • Homogenate mechanically

VARNISH POOL

Lacquered concentrate based on methacrylic resins for the completion of swimming pools and submerged areas with excellent grip strength. Unalterable to water and detergents, and with good resistance to alkalis, acids and dilute salts, as well as oils, petroleum and some alcohols.
To be diluted 40% with solvent pool.

Features:

  • Appearance: Semimate. In colorless gloss and satin.
  • Possibility of pigmentation.
  • Density: 1.27kg / ltr
  • Solids: 70%
  • Practical performance: 10 m2 / kg per layer (*) (depending on the type of support and conditions of application).
  • Drying time: At touch: 0.5 – 1 hour (at 20 ° C and 60% relative humidity):
  • Passable: People: 12 hours. Light vehicles: 48 h.
  • Heavy traffic and maximum resistance: 3 days
  • Repainting – approx. / 24 in case of being for submerged areas (pools rafts ..)
  • Number of layers: 2
  • Storage stability: 1 year in original container, indoors, between 5 and 40 ºC.

PRECAUTIONS

New Surfaces:
Wait for complete cure of the cement (approximately 1 month). The surface must be dry, clean and free of dust, grease, mold, seaweed and other contaminants. Brush, if necessary, to remove loose particles. If we can not wait for cement to cure, replace the applied VARNISH POOL with AQUA POOL
Apply a layer of EPOXI FIXER on inconsistent or absorbent surfaces.

Painted surfaces:
If paint is well adhered, brush to remove loose particles, clean and degrease. On shiny surfaces sand and apply a layer of EPOXY FIXER.

SOLVENT POOL

Pure solvent for mixing with Varnish Pool. Non-residual and retarded drying. Resistant to continuous PH from 2 to 12.

AQUA POOL

Water sealant to be applied to surfaces of porous materials and protect them from penetration of water, dissolved salts, oil stains.

Suitable for both indoor and outdoor use. Maintains natural color and surface finish. The treated surfaces are completely safe for contact with food. Excellent protection against water and oils.

Features:

  • Presentation: Containers of 4 Liters
  • Color: milky
  • Yield: 3 to 10 m2 / liter of product (according to support)
  • Curing time: minimum 12 days
  • Dry to the touch (20ºC):> 10 hours
  • Complete curing (20ºC):> 25 days
  • Depth of penetration: according to porosity of the material and climatology Composition: water-based aqueous emulsion
  • Density: Ca. 0.78 g / cm
  • Appearance: concentrated
  • Flash point: 100 ° C

PRECAUTIONS
The surface to be treated must be clean, solid, free of dust and free of badly adhered parts.
Surfaces must be completely dry before applying the product.
On recent cement surfaces, these must be cured for a minimum of 3 days.
The treated surface must remain unchanged (rain, ice, condensation) for a minimum of 24 hours, to ensure the performance of the product.
Avoid contact with moisture for 15 hours after application.
To clean sealed surfaces, use neutral PH detergents dissolved in warm water.

How to use:
Cover generously the whole surface, with roller, sponge …
Allow the product to penetrate at least 1 hour. Remove excess product with a dry polishing cloth or machine felt disc.
Use water to clean utensils used in the application. It can be moistened after 24 hours, wet after 3 days, filled with standing water (pool …) after 7 days.

VARNISH HIDROREPELENT (Antigraffitis)

High performance varnish based on aliphatic polyurethane resins and water-based, two-component polydimethylsiloxane. Hydrophobicity and oleophobia (water and oil repellency) increase dramatically.

For its great tension in the drying, always apply on surfaces primed and sealed. This product only provides the weather resistant, transit and anti-painted finish. Product not repaintable directly. For its repainting it is necessary to physically wear its superficial layer, (a minimum of 30 μm).

If the surface is not smooth and the wear is not on the surface, adhesion in those areas will not be correct and scaling may occur.

One hand is recommended, with a performance of 120g / m².

Mechanical mixing of the catalyst at low revs. Minimum 4 minutes plus 2 minutes rest.

Application:
Apply a very thin layer to get the recommended performance.
With roller or brush, do not carry excess product.
With spray gun or low pressure pump, use nozzle for lacquers or lacquers, 12 to 15 μm.
Pot-live. 40 minutes at 20 ° C and 60% humidity.
Use first cement prior to placement diluted 1/1 with running water

Its low viscosity gives it a high penetration in closed pore supports to improve the anchoring and high consolidation power in mortars or other bad supports.

According to its use it is recommended one or two hands, with a yield of 100g / m² per hand. Respect a minimum drying time of 12 hours.
Mechanical mixing of the catalyst at low revs. Minimum 4 minutes, plus 2
Minutes of rest.

Features:

  • Presentation: 5 Liters
  • Specific weight ~ 1 g / cc.
  • Dry to the touch 1 hour.
  • Stability to frost Good.
  • Repainting According to support.
  • Aliphatic outdoor resistance
  • Resistance to saponification Good.
  • Adhesion Absorbent support.
  • Finish Gloss.
  • Recommended thickness 50 μm.
  • Yield ± 20m² / kg. According to surface.

HIDROREPELENT (Antigraffitis)

Water-repellent water-repellent 1/7 with tap water. Not stain. Breathable. Do not create movie or alter appearance. Does not provide shine. Not repaintable. Anti-graffiti protection, it is necessary to repaint the surface every 18 months, or after cleaning. Self-cleaning powder surfaces.

Features:

  • Presentation: 25 Liters
  • Specific weight ~ 1 g / cc.
  • Dry to the touch 1 hour.
  • Stability to frost Good.
  • Optimal outdoor resistance
  • Repainting Hand on hand
  • Resistance to saponification Good.
  • Adhesion Absorbent support.
  • Finishing No residue.
  • Recommended thickness Nano membrane.
  • Yield ± 20m² / kg. According to surface.

VARNISH SANITARY

Coating based on 100% solids epoxy resins, formulated to be in contact with foodstuffs. Without solvents High chemical resistance In the interior of tanks and silos, both concrete and steel to contain oils, wines, preserves … Protection of floors in sanitary, meat, pharmaceutical laboratories…

Features:

  • For food industry
  • For tanks and silos
  • Without gasket
  • Product approved by the Ministry of Health and Consumer Affairs.
  • Mix Life: 20-25 minutes
  • Dry to the touch (25ºC): Less than 2 hours
  • Drying without tack (25 ° C): Less than 6 hours
  • Time between layer and layer: minimum 12 hours to maximum 24 hours
  • Complete curing (25ºC):> 7 days
  • Complete curing (15ºC):> 12 days
EPOXY

PRIMER VARNISH

CONDITIONS OF IMPLEMENTATION

  • On a completely dry and moisture-free surface, clean and free of grease and other materials.
  • Do not apply with relative humidity higher than 85% and ambient temperature below 15ºC.
  • Maximum support humidity <4%.
  • In the preparation to ensure a good anchorage, mechanical milling, sand blasting … is recommended before application.
  • Apply with good renewal of air, 100% solids free of solvent
  • On fully cemented cementitious bases

On smooth, non-absorbent surfaces, open pore
By mechanical means (abrasive blasting,
Abrasive disk) accompanied by
A deep aspiration.

RESISTANCE TABLE

  • Temperature dry heat: 13ºC
  • Humidity temperature: 75 ° C
  • Salt Fog: Resistance> 1000 hours
  • Diluted acids: Resistance> 1 year
  • Diluted alkalis: Resistance> 1 year
  • Marine environment: Resistance> 3 years
  • Industrial environment: Resistance> 3 years
  • Water immersion: Resistance> 5 years
  • Saltwater immersion: Resistance> 5 years
  • Resist 20ºC below zero

EMPLOYMENT CHARACTERISTICS

  • Mix Life: 15 minutes
  • Mixing example 1 kg: 0.725 kg component A 0.275 kg component B
  • Drying at 20 ° C and relative humidity 60%
  • Dry to the touch: 60 min.
  • Total drying: 6 hours
  • Total Polymerization: 7 days
  • Final appearance: bestowed

* These times are contemplated at 20ºC and may vary depending on the ambient temperature.

Features:

  • Composition: Bicomponent epoxy resin
  • Weight of the mixture: 1.1 g / cm3
  • Glossy finish
  • Viscosity: 70-80 U. / KREBS
  • Absorption on concrete: 2.2 N / mm2
  • Compression resistance at 7 days of Epoxy mortar (1 part of Pavidur 2 comp. Primer + 8 parts of selected Arid): 55 MPa
PRINTED MORTAR

VERTICAL TEXTURABLE

Continuous monolayer coating for decorative finish of facades and outdoor protection in outdoor / indoor.

Features:

  • Presentation: in paper bags of 25 kg anti-humidity.
  • Pallets of 48 bags.
  • Yield: 1.6 kg / m2 and mm thick
  • Kneading water: 17%
  • Resting time after kneading: 5 min.
  • Maximum thickness tolerated: 50 mm.
  • Maximum thickness per layer: 25 mm.
  • Minimum thickness after finishing: 12 mm.
  • Minimum thickness on thermal insulation board: 5-7 mm.
  • Time to texture: 30 -90 minutes.
  • Adhesion thickness 1 cm: 0.9 MPa
  • Compressive strength (28 days): 18 N / mm2
  • Resistance to flexion (28 days): 5.6 N / mm2
  • Determination of dimensional stability: 0.01%
  • Thermal conductivity (10 ° C): 0.72 W / mK (P = 90%)
  • Water absorption: 250 ºC without mechanical deterioration.
  • Determination of PH: 12.6

* Tests according to European standard UNE-EN-998-1

TEXTURABLE RECYCLING FLOORS

Continuous colored flooring for screeds of 5 to 50 mm, Road and pedestrian traffic of Interior and exterior Decorative finishes, High performance. Bombeable. For stamped, smooth, frosted or scratched finish.

Features:

  • Kneading at 14%
  • Yield: 2 kg / m2 and mm thick
  • Mix Life: 40-50 minutes
  • Open time: 20-30 minutes
  • Thickness between 10 and 50 mm.
  • Drying time: from 5 to 6 hours
  • Start-up: from 24 to 36 hours
  • Ice-thaw with salts UNE-EN 1339: Ap. 5.9: 0.16 kg / m2
  • Compressive strength:> 20.0 N / mm2
  • Resistance to bending:> 6.0 N / mm2
  • Adhesion to support: 1.8 N / mm2
  • Impact resistance UNE-EN 12633:
  • Drop height:> 1500 mm
  • IR value: IR = 14.7 N · m
  • Wear resistance: Sliding according to CTE: Class 3

* Tests according to European standard UNE-EN 13813: 2003

COLOR QUARTZ

High-strength colored quartz that is applied on the fresh concrete and that allows the molding of the concrete offering a layer of rolling of excellent hardness and durability. For the decoration of traditional flooring (paving stone, wood …) Especially suitable for urban pavements, dwellings, car parks…

Features:

  • Presentation: in paper bags of 25 kg anti-humidity.
  • Pallets of 48 bags.
  • Wear to abrasion: 20 mm.
  • Water Absorption: 7%
  • Slip Resistance: CRD – 0.52
  • Application by dusting in 2 passes, on the fresh concrete.
  • The mortar must be completely integrated on the fresh concrete.
  • Avoid wetting the concrete with water.
  • In heat times to delay the process of setting the concrete with liquid retardant
  • In winter time accelerate the setting of the concrete with liquid accelerator
  • After the first 24 hours approx. Open expansion joints in cloths of maximum 16-20 m2.

RELEASE AGENT

Demoulding powder for concrete and mortar stamps. It prevents the mortar from sticking to the mold. It is used to age the pavement or facade. For immediate demoulding Do not stick to the mold To age the floor. Excellent performance.

Features:

  • Presentation: in paper bags of 25 kg anti-humidity.
  • Pallets of 48 bags.
  • Yield: 80-100 grams / m2
  • Solubility in water: insoluble
  • Decomposition temperature: 250 ° C
  • PH: 8-9 (50 g / L water)
  • Not toxic

* Consult catalog of molds

THEMATIC ROCK

Thematization of carved stone, rock … Rehabilitation of facades and walls. Coronation of pools of multiple finishes and imitations. Great resistance and durability. Waterproof and breathable.

Features:

  • Presentation: in paper bags of 25 kg anti-humidity.
  • Pallets of 48 bags.
  • Kneading: l 17% of the total mass.
  • Yield: 14-17 kg / m2 and cm thick
  • Color: according to letter
  • Resting time after kneading: 5 min.
  • Maximum thickness tolerated: 20-25 cm.
  • Maximum thickness per layer: 5 cm.
  • Mixing time between 30 and 60 minutes.
  • Density in powder: 1.3 g / cm3
  • Mass density: 1,890 kg / cm3
  • Density of hardened product: 1,887 kg / cm3
  • Flexural strength: 4.4 N / mm2
  • Compressive strength: 15.1 N / mm2
  • Water retention: 97%
  • Elastomer: 10,082 MPa
  • Determination of PH: 12.1
MORTAR & MONOLAYER

FINE MORTAR

Dry mortar for masonry works in general, masonry, plaster for painting

Features:

  • Presentation: in paper bags of 25 kg anti-humidity.
  • Pallets of 48 bags.
  • Yield: 18 kg / m2 and cm of thickness
  • Resting time after kneading: 5 min.
  • Maximum thickness tolerated: 50 mm.
  • Maximum thickness per layer: 25 mm.
  • Minimum thickness: 10 mm.
  • Open time: 1-2 hours.
  • Density of fresh mortar: 2037kg / m3
  • Workability time: 175 minutes
  • Resistance to flexotraction: 4.1 N / mm2
  • Compressive strength: 6.5 N / mm2
  • Chlorides: 0.01%

MONOLAYER

Continuous monolayer coating for decorative finish of facades and protection against the intemperie in exteriors and interiors. Special Scraped or fratasado.

Features:

  • Presentation: in paper bags of 25 kg anti-humidity.
  • Pallets of 48 bags.
  • Yield: 1.6 kg / m2 and mm thick
  • Knead with 17% clean water.
  • Resting time after kneading: 5 min.
  • Maximum thickness tolerated: 30 mm.
  • Maximum thickness per layer: 15 mm.
  • Minimum thickness after scraping / fracturing: 10 mm.
  • Scraping time: 4-15 hours.
  • Density in powder: 1,500 kg / m3
  • Bulk density: 1,896 kg / m3
  • Density of hardened product: 1,887 kg / m3
  • Adherence: 0.66 N / mm2
  • Water permeability: 0.28 ml / cm2
  • Determination of PH: 12.1

* Tests according to European standard UNE-EN 998-1

ACRYLIC MORTAR

CREPI (STUCK, STRIPED, SMOOTH AND RUGGED

Monocomponent acrylic mortar for decorative finishing of facades and vertical walls.
Rendimineto of 4 kg m2 with smooth rough finish chopped and scratched.
PÉTREO COATING

GRANITE

High performance synthetic mineral coating for the decoration of all types of exterior and interior façades. Repellent to water and dirt, Anti-mildew-anti-verdin, Water-repellent, Suitable for walls and ceilings, not pick up. Compatible with most media. It systematically blocks micro capillary fissures.

Features:

  • Thickness of application of 2 to 3 mm per layer.
  • Dry to the touch: 6-7 hours
  • Total hardening time: 16-17 hours
  • Density of the paste: 1700 kg / ltr.
  • Drying Retraction: 4.50 mm / m
  • Capillary absorption of water: 0.04 kg (m2.min 0.5)
  • Adherence: 2.00 N / mm2
  • Fire behavior: not combustible
  • Insensitive to marine atmospheres
  • Insensitive to acid rain
  • Insensitive to carbon dioxide pollution
  • Absolutely odorless once polymerized

* Tests according to EC Standard * UNE-EN1015

SPORTS ACRYLIC PAINTING

SPORTS PAINTING

For sports courts, pediments and multi sports. Excellent coverage and adhesion with sliding effect. Ecological without pollution to the environment. On smooth, non-absorbent surfaces … sand before and open pore, to ensure a good anchorage.

Features:

  • Presentation: 22 kg containers Pallets of 792 kg (36 containers)
  • Yield: 6-8 m2 / kg approximately (1 layer)
  • Application temperature: 5-30ºC
  • Viscosity (22 ° C): 80 dPa.s
  • Specific weight: 1.40 kg / l
  • Gloss: satin
  • Drying time to touch: 30 min.
  • Repainting: 8 hours minimum
  • Shake to a perfect homogenization:
  • First layer: dilute 10-15% with water.
  • Other layers: dilute between 5-10% with water.
  • Apply with the right tool, roller, brush, airless …
  • Yield ± 20m² / kg. According to surface.
RUBBER FOR GARDENS

RUBBER PAVEMENT

  • Complies with the safety regulations in playgrounds EN-1177
  • Maximum protection and reduction of damages caused by falls, pavement security.
  • Stretchy and pleasant to the foot tread, ideal for areas of footpaths and pedestrian rails.
  • 100% Free of harmful substances.
  • Anti-slip action: Provides a completely non-slip surface even with presence of water.
  • Good drainage of water, has a structured base to evacuate the water and a quick drying without leaving puddles.
  • Resistant to outdoor use, it resists sun, water, snow and other adverse weather conditions.
  • Green product, for sustainable development.
SAND BEACH

SAND BEACH

Composite stone for creating pools with sand beach effect.

Features:

  • Component stone A 30 kg (+/- 5 m2)
  • Resin component B in 25 liters (+/- 50m2)
  • Colors: white and sand (also colors à la carte)

* Refer to systems guide.

WATERPROOFING AND INSULATION

ELASTIC

Flexible and impermeable bicomponent mortar (20 kg + 10 Liters) to correct supports with retraction fissures with two layers and intermediate mesh in both mortar, wood, parquet, parquet, plaster, self-leveling mortar …. Resistance to positive pressure. Waterproofing of concrete tanks for water, including drinking water. Waterproofing of showers, baths, swimming pools … Waterproofing of concrete surfaces exposed to the action of water and to the chemical aggression of external agents, such as salts, de-icing, chlorides … Apply 2 hands with 80 gr intermediate mesh.

Features:

  • Presentation: Anti-humidity paper bags of 20Kg + 10 Liters.
  • Color: White and Gray
  • Dosing component A + B (2/1)
  • Resting time after kneading: 5 min.
  • Mix Life: 60 minutes
  • Application thickness: 2 mm per layer
  • Start of setting: 4 hours
  • Intercoat timeout: 4-5 hours
  • Wait for tank filling: ≥28 days
  • Coated – painting:> 6 days
  • Apply in temperatures between 10º and 30º
  • Do not apply with risk of rain or strong wind
  • Traction adhesion: ≥1.5 MPa
  • Dilution index: ≤3
  • Dilution odor: ≤5
  • Conductivity: (μS / cm) 325
  • PH (μPH): 8.4
  • Properties in traction:
  • Strength: 1.6 MPa
  • Elongation: 65%

* Certificate of Potability

PLASTIC PRESS

Elastic and impermeable mortar for exterior waterproofing, repairs and waterproofing cracks, suitable on supports with small movements. Machine-designed, Water resistant. Suitable for receiving paint or cementitious coating. Resistant to contact with aggressive waters. Spectacular resistance to negative pressure.

Features:

  • Bulk density: 1.3 g / cm3
  • Density in paste: 1.6 g / cm3
  • Compression:> 30 N / mm2
  • Flexion:> 6 N / mm2
  • Determination of transverse deformation: 2.5 mm
  • Impermeability
  • DIN 1048: waterproof
  • Adhesion on concrete: 1.6 MPa

SISTEMA SATE

High performance mortar formulated for the placement and regularization of thermal insulation boards in exteriors, to be able to finish with acrylic mortars, monolayer mortars, micro cement…

Features:

  • Presentation: in paper bags of 25 kg anti-humidity.
  • Pallets of 48 bags.
  • Resting time after kneading: 5 min.
  • Plate rectification time: 15 min.
  • Dough life: 1-2 hours approximately.
  • Thickness per layer: 3-5 mm
  • Density in powder: 1,400 kg / m3
  • Kneading water: ± 25%
  • Density in paste: 1,600 kg / m3
  • Water retention: 99%
  • Lift with piece of 10 kg: 0mm
  • Adhesion (28 days): 1 N / mm2
  • Resistance to bending: 4.5 MPa
  • Compressive strength: 9.4 MPa
  • Transverse deformation: 2.8 mm
  • Flammability: MO

RUBBER ANTIGOTERS

Waterproofing of terraces, decks, facades … Compatible with fiberglass mesh reinforcements. Resistant to aging and ultraviolet rays. Abrasion resistant and washable. Resistant to ultraviolet rays.

Features:

  • Presentation: cubes of 16 Liters
  • Color: red, green, white and gray. Others consult.
  • Preparation: 1 hand dilute 15% max with water, pure residue.
  • Application temperature: 5-30ºC
  • Viscosity: 100 dPa.s
  • Density: 1.34 g / cc
  • Drying time to touch: 60 min.
  • Drying time between layers: 24-36 hours
  • Elongation:> 250%
ADHESIVES TILES

GENERAL CONDITIONS

PERFORMANCE

  • Simple bonding: 3-4 kg / m2
  • Double gluing: 5-6 kg / m2
  • The wind causes a shorter open time of the mortar and leads to a lower adhesion.
  • Do not apply with risk of rain in the exterior, nor with humidity above 3% indoors.
  • In exterior soils the support must have a minimum of 1% of slope for the evacuation of the water.
  • In floors with radiant heating, it must be turned off 48 hours before.
  • On plasterboard, check the level of rigidity of the partition.
  • Do not apply tile, stone, marble … in the form of “touches”.
  • Application temperature 5 ° C to 30 ° C
  • On façades, make expansion joints every 30-60 m2 according to format, as well as perimetral joints on cornices, forged …
  • During placement, avoid water seepage between the support and the workpiece.
  • Protect the top edges of the final lining with cornices, flushing …
  • In facades of ceramic coating leave 5mm gasket. At least and fill with (Wide Joint).
  • The support must be resistant, completely set and free of dust, oil, grease …
  • Heal the disintegrable parts.
  • Use mesh between supports of different nature.
  • On substrates exposed to the sun or very absorbent it is recommended to wet them previously.
  • On the basis of cement, concrete … these must be completely set (≥ 28 days).
  • In large format coatings (≥ 40 kg / m2) it is essential to use mechanical anchorage.
  • Knead with running water until a homogeneous mass is obtained and free of lumps.
  • Mix with a slow speed beater.
  • Let stand 5 minutes.
  • Extend the material with a notched trowel in small cloths (maximum 2m2)
  • Double glue for large format and high weight pieces.
  • Lay the tiles, pressing and moving from top to bottom to get the crushing of the grooves of the mortar glue.
  • Before placing the ceramic check that the cement glue has not formed a surface film since it would prevent its adhesion. If so, re-comb with trowel.

CE

Thin layer glue mortar for laying tiles, ceramic, stoneware, medium and high porosity. In pavements and interior linings.

Features:

  • Presentation: in paper bags of 25 kg anti-humidity.
  • Pallets of 48 bags.
  • Mixing water: ± 24% (6/7 liters of water)
  • Density of mass: 1600 kg / m3
  • Water Retention: 98%
  • Initial adhesion: ≥ 0.5 N / mm2
  • Adhesion after immersion: ≥ 0.5 N / mm2
  • Sliding ≤ 0.5 mm

C1TE

For the placement of ceramic tiles, with or without absorption, small and large format, especially for the placement of porcelain stoneware in interiors. On exterior and interior floors. Suitable for diving. Suitable for swimming pools

Features:

  • Presentation: in paper bags of 25 kg anti-humidity.
  • Pallets of 48 bags.
  • Kneading: 6/7 liters of water
  • Resting time after kneading: 5 minutes
  • Approximate Rectification Time: 30 minutes
  • Pasta life: 4 hours approximately
  • Density of mass: 1700 kg / m3
  • Water retention CSTB: 99.0%
  • Initial adhesion: ≥ 0.5N / mm2
  • Adhesion after immersion in water: ≥ 0.5 N / mm2
  • Adhesion after freeze-thaw cycles: ≥ 0.5 N / mm2
  • Adhesion after heat aging: ≥ 0.5 N / mm2
  • Adhesion open time: ≥ 0.5 N / mm2
  • Slip: ≤ 0.5 N / mm

* Tests according to UNE-EN 12004

C2TE

Mortar glue flexible white – gray in thin layer for the coating of facades and pavements of intense traffic, with ceramic, marble, natural stone … with or without absorption, small and large format. In exterior and interior. Underfloor heating floors.

Features:

  • Presentation: in paper bags of 25 kg anti-humidity.
  • Pallets of 48 bags.
  • 5.5-6 liters of water
  • Initial adhesion: ≥ 1N / mm2
  • Adhesion after immersion: ≥ 1N / mm2
  • Adhesion after heat aging: ≥ 1N / mm2
  • Adhesion after freeze-thaw cycles: ≥ 1N / mm2
  • Open time adherence 30 minutes: ≥ 0.5N / mm2
  • Sliding: ≤ 0.5N / mm2
  • Deformation: ≥ 2.5mm
  • Water retention CSTB: 99.0%

* Tests according to UNE-EN 12004

C2TE S1

High-performance white-gray glue mortar for coating floors and facades of large surfaces with ceramic, porcelain stoneware and natural stones of large format, absorbent and non-absorbent, as well as for gluing insulation materials such as rock wool , Extruded wood fiber, expanded polystyrene … Indoors and outdoors. Underfloor heating floors.

Features:

  • Presentation: in paper bags of 25 kg anti-humidity.
  • Pallets of 48 bags.
  • Initial adhesion: ≥ 1.0 N / mm2
  • Adhesion after immersion in water: ≥ 1.0 N / mm2
  • Adhesion after heat aging: ≥ 1.0 N / mm2
  • Adhesion after freeze-thaw cycles: ≥ 1.0 N / mm2
  • Adhesion open time: ≥ 0.5 N / mm2
  • Deformation: ≥ 5 mm
  • Sliding: ≤ 0.5 mm
  • Deformation: ≥ 2.5 mm

* Tests according to UNE- EN 12004

C2TE S2

High-performance white-gray glue mortar for coating floors and facades of large surfaces with ceramic, porcelain stoneware and natural stones of large format, absorbent and non-absorbent, as well as for gluing insulation materials such as rock wool , Extruded wood fiber, expanded polystyrene … Indoors and outdoors. Underfloor heating floors.

Features:

  • Presentation: in paper bags of 25 kg anti-humidity.
  • Pallets of 48 bags.
  • Initial adhesion: ≥ 1.0 N / mm2
  • Adhesion after immersion in water: ≥ 1.0 N / mm2
  • Adhesion after heat aging: ≥ 1.0 N / mm2
  • Adhesion after freeze-thaw cycles: ≥ 1.0 N / mm2
  • Adhesion open time: ≥ 0.5 N / mm2
  • Deformation: ≥ 5 mm
  • Sliding: ≤ 0.5 mm

* Tests according to UNE-EN 12004

PUTTY FOR TILES

MORTAR OF GATHERING

Colored mortar for filling joints between tiles from 1 to 30 mm, in any type of pavement, ceramic coating.

Features:

  • Excellent workability
  • Without fissures
  • Waterproof
  • Mixing between colors is supported
  • Resting time after kneading: 5 minutes
  • Maximum cleaning time: 30-60 minutes
  • Dough life: 60 minutes
  • Start-up time: 3-4 days

* Consumption can vary depending on the thickness and width of the joints, as well as the dimensions of the ceramic material.

FINE JOINT

Colored mortar for filling joints up to 3mm wide between ceramic pieces and in any type of flooring or cladding. Indoors and outdoors.

Features:

  • Presentation: 5 kg
  • Apparent density powder: 1 ± 0.1 g / cm3
  • Kneading water: 35%
  • Density of mass: 1.6 g / m3
  • Capillarity: 2 g / dm2 · min½

WIDE BOARD

Colored mortar for filling joints between tiles from 3 to 15 mm, in any type of pavement, ceramic coating. Mortar for application in paste form. Indoors and outdoors. Underfloor heating floors.

Features:

  • Presentation: 5 kg
  • Apparent density powder: 1.4 g / cm3
  • Kneading water: 25%
  • Density of mass: 1.8 g / m3
  • Lower capillarity: 0.5g / dm3 · min½

REFRACTORY MORTAR

Special mortar for the assembly and anchoring of refractory brick, solid or hollow block, terracotta, which are subjected to high temperatures: barbecues, wood ovens, fireplaces … For the assembly and grouting of masonry work in contact with aggressive waters or Acids, food industries, sewage pipelines, sanitation and industrial waste. Indoors and outdoors.

Features:

  • Presentación: Sacos de papel antihumedad de 25 kg.
  • Palets de 48 sacos.
  • Color: gris oscuro.
  • Amasado: 15 % de agua.
  • Tiempo de reposo después del amasado: 2 min.
  • Tiempo vida de la masa: 40 minutos
  • Tiempo de corrección: 20 minutos
  • Inicio de fraguado: 4-5 horas
  • Puesta en marcha: 4-5 días
  • Densidad en polvo: 1.5 g/cm3
  • Retracción < 0.7 mm/m Adherencia > 0.3 MPa
  • Flexotracción > 5 MPa
  • Compresión > 40 MPa
  • Módulo elasticidad: 35000
  • Temperatura máxima de resistencia térmica: 800 ºC

MATERIALS / TOOLS